Aluminum Sheet, Magnesium Alloy Plate, Aluminum Plate manufacturer / supplier in China, offering Anti-Rust Aluminium Magnesium Alloy for Electronics, Checkered Aluminum Coil with 5 Bars, 3003 Aluminum Coil for Kitchen Utensils and so on.

(/ )

Supplier Homepage Product Aluminum sheet Anti-Rust Aluminium Magnesium Alloy for Electronics

Anti-Rust Aluminium Magnesium Alloy for Electronics

FOB Price: US $2,640 / Ton
Min. Order: 2 Tons
Min. Order FOB Price
2 Tons US $2,640/ Ton
Get Latest Price
Production Capacity: 6000tons/Month
Transport Package: Wooden Pallet
Payment Terms: L/C, T/T, D/P

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: HL-S061
  • Application: Decorations, Heat Sink, Transportation Tools, Door & Window, Glass Wall
  • Grade: 5000 Series
  • Technique: Mill Finished
  • Temper: O - H112
  • Width: 200-2350
  • Origin: China
  • Type: Aluminum Sheets
  • Shape: Flat
  • Surface Treatment: Mill Finish
  • Alloy: Alloy/Non-Alloy
  • Thickness: 0.2-500
  • Trademark: HANLV
Product Description
Specifications
Aluminium magnesium alloy:
1, be prime quality fully certified to ASTM & AMS specifications
2, helpful & knowledgeable sales
Specification:

5XXX series aluminium alloys, with magnesium as the major alloying element, combine a wide range of strength, good forming and welding characteristics, and high resistance to general corrosion.

Strength
Generally increases with increasing magnesium content, and can be further enhanced by cold work.

Forming
5XXX aluminium alloys are easily cold formed. Formability being described by minimum cold bend radii. Formability tends to increase as alloy strength decreases.

Welding
5XXX aluminium alloys are easily welded using GMA-W or GTA-W processes. Weld strength equals the minimum annealed strength (O temper) of the welded 5XXX alloy. Welds also show good ductility, facilitating cold forming.

Corrosion Resistance
5XXX aluminium alloys generally have excellent corrosion resistance, often being used in marine applications e. G. 5083-H116.
5XXX series aluminium alloys with greater than 3.5% magnesium (e. G. 5086 & 5083) may be susceptible to stress corrosion cracking (SCC). In service, limitations should be placed on the amount of cold work and maximum permissible operating temperature for the higher magnesium alloys to avoid increased susceptibility to stress corrosion cracking and intergrannular corrosion.
Such alloys should not be used at operating temperatures >65° C. 5454 and 5754 are manufactured with 2.7% and 3.1% magnesium respectively and are designed for use at elevated temperatures.

Availability
5XXX aluminium alloys are most commonly available in F (as rolled) or O/H111 (fully soft) condition, although cold worked tempers such as H32, H321 and H116 are also available.


Application: Construction, decoration, automobile, electronic, machinery, boat construction, aeronautics & astronautics, cookware, packing etc.
Chemical composition
Alloy (%) 5052 5083 5086 5754
Si 0.25 0.40 0.40 0.40
Fe 0.40 0.40 0.50 0.40
Cu 0.10 0.10 0.10 0.10
Mn 0.10 0.40_ 1.0 0.20_ 0.7 0.50
Mg 2.2_ 2.8 4.0_ 4.9 3.5_ 4.5 2.6_ 3.6
Cr 0.15_ 0.35 0.05_ 0.25 0.05_ 0.25 0.30
Ni _ _ _ _
Zn 0.10 0.25 0.25 0.20
Ti _ 0.15 0.15 0.15
Each (Others) 0.05 0.05 0.05 0.05
Total (Others) 0.15 0.10 0.10 0.15
Al Remaining Remaining Remaining Remaining
                                                                                                             Single number indicates maximum content.
Send your message to this supplier
Avatar
Ms. Fay Yang
*From:
To: Ms. Fay Yang
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category