5083 H116 3mm 4mm 5mm 6mm Marine Aluminum Sheet

• Customization: Available
• Application: Transportation Tools, Heat Sink, Decorations
• Certification: ISO9001, Astmb, ASTM, JIS
• Model NO.: HL-0325-6
• Technique: Hot Rolling
• Grade: 5000 Series
• Temper: O - H112
• Surface Treatment: Mill Finish
• Alloy: Alloy
• Thickness: 2-300mm
• Width: 200-2500
• Type: Aluminum Sheets
• Shape: Flat
• Transport Package: Wooden Pallet, Wooden Box
• Specification: SGS, ROHS
• Trademark: HANLV
• Origin: Zhejiang
• HS Code: 76061259
• Production Capacity: 600 Tons /Day

Product Description

5083 H116 3mm 4mm 5mm 6mm Marine Aluminum Sheet

  

Description	5083 H116 3mm 4mm 5mm 6mm Marine Aluminum Sheet
Alloy	5083
Temper	O,H111, H112, H116, H321
Thickness (MM)	0.2~500
Width (MM)	200~3000
Length (MM)	≤12000
Application	Marine/Boat/Automobile parts, Oil Tank, Pipe; Construction, Electrical cabinet, Parts; Hardwares, Electric Appliance, etc.

 Basic Information GB/T 3190-1996

Chemical Composition
Aluminum Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Others		Al
									Single	Total
5083	0.082	0.27	0.013	0.515	4.33	0.086	0.007	0.018	0.05	0.15	The Rest
Features
With Mg as its main minor ingredient, 5083 has good anti-rust quality,formability, good cold workability, welding quality and better strength.
Application
Wide application especially in marine Industry; Boat/Automobile parts, Oil Tank, Pipe; Construction, Electrical cabinet, Parts; Hardwares, Electric Appliance, etc.

Factory tour for 5083 H116 3mm 4mm 5mm 6mm Marine Aluminum Sheet:

 Rolling begins with huge sheet ingots weighing as much as 20 tons that have been preheated to make them easier to shape. As the size of rolling mills has increased, so has the size of these ingots, but a typical ingot is about 1828mm wide, 6096mm long, and more than 610mm thick.
    The ingot is first fed into a breakdown mill, where it is rolled back and forth, reversing between the rolls until the thickness has been reduced to just a few inches. At this point, some plate is removed and readied for shipment. The plate is heattreated and quickly cooled, or quenched, for added strength and then stretched to straighten and relieve internal stress built up during rolling and heat-treating. Finally, the plate is trimmed and aged at the desired temperature to develop its final properties.
    Plate that is slated to become sheet or foil is trimmed after leaving the breakdown mill and sent through a continuous mill to reduce thickness further. Sheet thicknesses are then coiled.
    To continue its reducing process, the coiled sheet is heated in a furnace to soften it for cold rolling. Cold rolling is the last step for some sheet. But other types, known as heat-treatable, are subjected to further elevated-temperature processing to increase their strength. 

Package for 5083 H116 3mm 4mm 5mm 6mm Marine Aluminum Sheet: In strong wooden pallets fumigated with strong steel hoops in all sides to withhold rough handling at port of export and port of imports.